Early age volume changes in concrete due to chemical shrinkage of cement paste, Cambios volumétricos a edad temprana en el hormigón debido a la retracción química del cemento

  • Ebensperger, L.
  • Breitenbücher, R.
  • Springenschmid, R.
Unrestrained early age volume changes due to chemical shrinkage in cement pastes, mortars and concretes have been determined. The measurements were performed on sealed and unsealed samples which were stored under water. The chemical shrinkage of unsealed specimens represents the amount of absorbed water due to the chemical reaction of the cement It depends only on the cement content of the sample and does not lead to changes of the external dimensions. However the chemical shrinkage of sealed specimens is connected with a real volume change due to self-desiccation and the effect of internal pressures. The shrinkage depends in this case on the restraining effect of coarse aggregates as well as the cement content. The chemical shrinkage measured on sealed concretes was much higher than the one expected to ocurr on concretes, because normally an equalization of pressure takes place to some extent in the interior of the concrete. The use of expansive additives showed that they may compensate the chemical shrinkage, but its dosage is very sensitive and should be defined exactly for each case particularly., Se han determinado los cambios volumétricos que ocurren en pastas de cemento, morteros y hormigones a edad temprana debido al efecto de la retracción química. Las mediciones se realizaron en probetas selladas y no selladas sumergidas bajo agua. La retracción química en probetas no selladas representa la cantidad de agua absorbida debido a la reacción química del cemento. Depende solamente del contenido de cemento de la probeta y no produce ningún cambio en las dimensiones de la probeta. Por el contrario, la retracción química en probetas selladas está relacionada con un cambio volumétrico real debido al efecto de la autodesecación y presiones internas. La retracción en este caso depende tanto de la restricción que imponen los áridos, como del contenido de cemento. La retracción química medida en hormigones sellados resultó ser mucho mayor que la que se espera ocurra en el hormigón, dado que en el interior del hormigón ocurre, hasta cierto grado, un equilibrio de las presiones desarrolladas. El uso de aditivos expansivos mostró que sí es posible compensar la retracción química, pero su dosificación es muy sensible y debe definirse exactamente para cada caso en particular
Proyecto:


Macroscopical morphology of deterioration of the stone in the cathedral of Guadíx/Spain, Morfología macroscópica de alteración de la piedra de la catedral de Guadíx/España

  • Alcalde, M.
  • Martín, A.
The main factors of deterioration that affect the Cathedral of Guadíx are of a natural origin, basically thermic and hydraulic, due to its great oscillations in temperature in Summer, the frequency of frosts in Winter and the rains. The lithotypes employed are mainly calcarenite of mean porosite and slightly more compact limestones from the quarries in the area, and marbles. The corresponding deterioration mechanisms are those of differential thermic dilatations caused by thermic jumps, especially in the more compact stones, those of increase in volume in capillaries and interstices, especially by freezing, and those of dissolution. The most serious deterioration indicators are fissures and spalling that affect the most carved elements and which have taken the greater part of the most aerated elements such as the pinnacles to a state to ruin., Los principales factores de alteración que afectan a la catedral de Guadix son de origen natural, fundamentalmente térmico e hidráulico, por sus grandes oscilaciones de temperatura en verano y por la frecuencia de heladas en invierno, y por la lluvias. Los litotipos empleados son principalmente calcarenitas de porosidad media y calizas algo más compactas, procedentes de canteras de la zona, y mármoles. Los mecanismos de alteración correspondientes son los de dilatación térmica diferencial originados por los saltos térmicos, en especial en las piedras más compactas, los de incremento de volumen en capilares e intersticios, sobre todo por heladicidad, y los de disolución. Los indicadores de alteración más graves son las fisuras y fragmentaciones que afectan a los elementos más labrados y que han llevado al estado de ruina a la mayor parte de los elementos más aireados como los pináculos.
Proyecto:


The use of fiy ash in concrete blocks, Elementos prefabricados de hormigón con cenizas volantes

  • Álvarez Alonso, Marina
  • Río Suárez, Olga
This paper describes how fly ashes which are not prescribed by the standards can be used in the manufacturing of concrete blocks. To implement this proposal it was necessary to do tests of the constitutive materials of the blocks, and block tests. The objective of these tests is to obtain the optimum blocks. This paper presents these tests and its main results., Se describe la posible utilización de cenizas volantes consideradas no aptas como sustituto del cemento por la normativa, que pueden ser utilizadas en otros sectores de la industria de la construcción como la de prefabricación de piezas de hormigón. Para ello, ha sido necesario realizar ensayos sobre los materiales constituyentes de los bloques así como de los propios bloques con el fin de obtener cuál es el elemento de hormigón más idóneo. En este artículo se presentan estos ensayos así como los principales resultados obtenidos.
Proyecto:


Durabilidad del hormigón: Acción del agua de mar sobre un cemento portland resistente a los sulfatos. Influencia de la adición de escorias y de cenizas volantes, Durabilidad del hormigón: Acción del agua de mar sobre un cemento portland resistente a los sulfatos. Influencia de la adición de escorias y de cenizas volantes

  • Gaspar Tebar, Demetrio
  • Sagrera Moreno, José Luis
  • González Vila, Victoriano
  • Marín Bohorouez, Miguel
This article, is part of a long time ICCET investigation programs studies the variation of the mechanical resistance to flexotraction 1: 3 normalized mortar with 1 x 1 x6cm dimension, using sulphate-resistent portland cement mixed with 15-35-60 and 70% parts of a furnace slag, a fiy ash or silica sand. The samples were submitted to the action of AS.T.M. artificial sea water and filtered potable water during several time periods (3 years for the first and second addition and 1 year for the third) after the cured period (1 day at 100% R.H. and 21 days inside filtered potable water). The evolution of the ionic concentration of the aggressive solutions were studied and also the new phases formed with its new structural composition. Finally, and account is given of the researches and first results about the behavior of the mortars and concretes made with two different industrial cements and submitted to the natural sea water at a selected area of the marine Huelva-Port., En este artículo, que forma parte de un Proyecto de Investigación del ICCETa largo plazo, se estudia la variación de las resistencias mecánicas —a flexotracción— de las probetas de mortero normalizado (1:3), de 1x1x6 cm, mezclando un cemento portland resistente a los sulfates y sus mezclas (cemento/adición = 85/15 - 65/35 - 40/60 y 30/70, en peso), con una escoria, ceniza volante y arena silícea. Se someten a la acción de agua del mar artificial ASTM y de agua potable filtrada durante diversos períodos de tiempo (hasta 3 años para las dos primeras adiciones, y hasta 1 año para la tercera) después de la fase de curado (1 día en cámara húmeda y 21 días bajo agua potable filtrada). Se estudia la evolución de la concentración iónica de los medios en donde han estado sumergidas dichas probetas de mortero, las características químicas de las nuevas fases sólidas formadas y la composición estructural de estas nuevas fases sólidas. Por último, se da cuenta de los trabajos iniciados y de los resultados previos obtenidos —desde este punto de vista— en un lugar seleccionado del Puerto Autónomo de Huelva, en donde se están sometiendo a la acción del agua del mar diversas series de probetas de mortero y de hormigón, así como bloques de hormigón.
Proyecto:


The significance of curing in the future corrosion resistance of concrete structures, La importancia del curado en el comportamiento posterior frente a la corrosión de las estructuras de hormigón armado

  • López, W.
  • Feliu, S.
  • González, J. A.
  • Andrade, Mª. Carmen
Steel in contact with fresh concrete is covered by a layer of passivating oxydes due to the alkaline nature of the pore solution. The presence of oxygen plays an important role in this passivation process as well as in the corrosión one when is developped due to the ingress of aggressives, such as, chloride ions. In the present paper, results are commented on the behaviour found when oxygen is limited due to the concrete curing conditions, in a completely saturated chamber. Surprisely, the results indicate that the oxygen availability during the curing has a marked influence on the future corrosion beabieviour This allows to deduce that the mechanisms involved are not so simple as was currently accepted and that new specific tests are needed to clarify the controversial points., Cuando el acero se pone en contacto con el hormigón fresco, debido a la naturaleza alcalina de éste, el acero se recubre de una capa de óxidos pasivantes, que lo mantienen constantemente protegido. En este proceso juega un papel preponderante la presencia del oxígeno, que resulta también esencial para el desarrollo de los procesos de corrosión, cuando hay agresivos presentes (por ejemplo los cloruros). En el presente trabajo se comentan resultados de los cambios que se aprecian, tanto en el proceso de pasivación como de corrosión, cuando el acceso de oxígeno se limita, circunstancia que se produce cuando el hormigón se cura en condiciones de saturación de agua. Los resultados muestran que la disponibilidad de oxígeno durante el curado tiene una marcada influencia en la resistencia futura a la corrosión lo, que indica que los mecanismos no son tan evidentes como se pensaba y se necesitarán ensayos futuros específicos para aclarar todos los aspectos que ahora aparecen como contradictorios
Proyecto:


Study of water-repellent treatments applied on limestone from Andalusian Cathedrals, Evaluación de tratamientos de hidrofugación aplicados a piedras calizas de Catedrales Andaluzas

  • Villegas, R.
  • Vale, J. F.
  • Alcalde, M.
Five types of stone used in Andalusian Cathedrals have been treated with different water-repellent treatments, to evaluate the effects of this products. The stones studied are limestone, calcarenite and dolomite; the products applied are organosilicones and acrylics. In this work properties related with water access and movement through the stone have been measured and compared their values before and after the application of the treatments., Se han tratado varios tipos de piedra utilizados en Catedrales Andaluzas con diversos productos hidrófugos, con el fin de evaluar las características conferidas por los mismos. Los tipos de piedra son de naturaleza caliza, calcarenitas y dolomías; los productos son organosilícicos y acrílicos. En este trabajo se han medido las propiedades relacionadas con el acceso y movimiento de agua en la piedra, comparándose sus valores antes y después de la aplicación del tratamiento.
Proyecto: