Formación de hidroxiapatita, Ca5(PO4)3∙OH, en presencia de silicatos, Formación de hidroxiapatita, Ca5(PO4)3∙OH, en presencia de silicatos

  • Diouri, A.
  • Boukhari, A.
  • Aride, J.
  • Puertas, F.
  • Vázquez, T.
Hydroxyapatite Ca5(PO4)3OH (HAp) is a crystalline phase which has several applications within the domain of special cements. This phase takes an important role in the cement reactions for the reconstruction of skeletal functions (medical domain). It is used also to improve properties of dental material. On the other hand, it is investigated to develop chemically bonded ceramics. In this paper we study the formation of HAp with β-C2S and C5PS, using some compositions in the rich lime portion of the system CaO-SiO2-P2O5-H2O (at atmospheric pressure and open system). These compositions lie in the range of: CaO: 67-71 %; SiO2: 3-18%; P2O5: 9-29% (Wt%). The preparations are made using solid state reactions, with thermal treatment at open system. The identification of phases was carried out using X-ray diffraction, Infra-Red absorption and Differential Thermal Analysis. We delimit a spectroscopy little domain lies in the range of CaO-69,5-70%; P2O5-16,2-19,5%; SiO2-11,1-13,6%. Within this domain, the crystalline phases solid state compatibility at temperature near 1000ºC are HAp, β-C2S, C5PS., La hidroxiapatita, Ca5(PO4)3OH (HAp), es una fase cristalina que tiene diversas aplicaciones en el ámbito de determinados cementos especiales. Esa fase juega un importante papel en las reacciones de cementos utilizados en medicina para la reconstrucción defunciones del esqueleto. Se utiliza también para mejorar propiedades de materiales de aplicación odontológica. Por otra parte, se está estudiando para desarrollar conglomerantes cerámicos. En el presente trabajo se estudia la compatibilidad en estado sólido de la HAp con β-C2S y C5PS utilizando, a presión atmosférica y recinto abierto, composiciones en la zona rica en cal del sistema CaO-SiO2-P2O5-H2O dentro de los límites siguientes. CaO: 67-71 %; SiO2: 3-18%; P2O5: 9-29% (en peso). El tratamiento térmico se realizó en estado sólido y en atmósfera abierta. La identificación de las fases se realizó a través de Difracción de Rayos X, Espectroscopia de Absorción Infrarroja y Análisis Térmico Diferencial. Se define una pequeña zona del diagrama de composición: CaO=69,5-70%; P2O5=16,2-19,5%; SiO2=11,1-13,6%. En este campo las fases cristalinas compatibles en estado sólido, formadas a 1.000ºC, son HAp, β-C2S y C5PS.
Proyecto:


Stuccos and roman concretes of the Baelo Claudia city (Cádiz): Characterization and causes of decay, Estucos y hormigones romanos de la ciudad de Baelo Claudia (Cádiz): Caracterización y causas de deterioro

  • Puertas, Francisca
  • Blanco-Varela, María Teresa
  • Palomo, Ángel
This paper presents the study of the nature and conservation state of different stuccos and Roman concretes from the Roman city of Baelo Claudia (Cádiz). The chemical, mineralogical and microstructural compositions of the said materials have been established. Different causes of their decay have been found, among which we should emphasize the loss of the binding material (lime), basically due to the processes of partial solubilization; the lack of bond between the stuccos and the support stone, due to the different characteristics and properties of these two materials; and finally, the biological-type attack with the proliferation and colonization of different organisms in the said materials., Se ha estudiado la naturaleza y estado de conservación de distintos estucos y hormigones romanos procedentes de la ciudad romana de Baelo Claudia (Cádiz). Se ha establecido la composición química, mineralógica y microestructural de dichos materiales. Se han encontrado diferentes causas de su deterioro. Entre ellas, cabe destacar la pérdida del material ligante (cal), fundamentalmente motivado por procesos de solubilización parcial; la falta de adherencia entre los estucos y la piedra soporte, debido a las diferentes características y propiedades de ambos materiales; y finalmente, también al ataque de tipo biológico, con la proliferización y colonización de distintos organismos en dichos materiales.
Proyecto:


Los vidrios de baja emisividad, Los vidrios de baja emisividad

  • Olivares Santiago, Manuel
  • Olmo Escribano, Rafael
The use of low-emittance coating (low-E) glasses in Europe and the United States is not recent (they make use of them long since: 10-15years), nevertheless they are almost unknown in Spain, in all respects, in spite of being commercialized long since by different houses, specialists in these matters. We run into a lack of regulation about the qualities and stipulations these elements must comply with, since the regulations governing the thermal insulation of the buildings (CT-79) refers to the generic and peculiar qualities of the glazed openings, but these regulations do not approach the question of the real behaviour of the glazed openings with low-emittance glasses and other semi-transparent elements. The expenditure of energy and the lighting characteristics of the openings are not yet unforeseen, so far. These properties undergo a variation with regard to the base-glass or the support, due to the low-emittance coating. The article is organized in to three parts. The first part is the analysis of the functional characteristics and the lighting properties of the glasses from a general point of view. The second one explains what low-emittance glasses are, and the way of obtaining them (very briefly); according to the kind of process of obtaining the low-emission coating, the proceedings of low-emission glasses are gradually limited. Finally, the third part deals with the thermic characteristics of whole glazing, and specially with the glazed openings, from the point of view of a functional consistency for both glass and joinery., Aunque en Europa y EEUU el uso de los vidrios de baja emisividad no es reciente (se llevan utilizando unos 10-15 años), en España son prácticamente desconocidos desde el punto de vista teórico y práctico, a pesar de estar comercializándose desde hace varios años por las casas especializadas. Nos encontramos con un vacío normativo sobre las condiciones que han de cumplir, ya que la norma de acondicionamiento térmico de los edificios (CT-79) hace referencia a propiedades genéricas de los huecos acristalados, pero no está suficientemente aproximada al comportamiento real de los huecos acristalados con vidrios de baja emisividad y otros elementos semitransparentes. No es frecuente todavía considerar el comportamiento energético y las características luminosas de los huecos. En los vidrios de baja emisividad estas propiedades ópticas sufren una variación con respecto al vidrio base o soporte debido a la capa de baja emisividad. Este artículo está estructurado en tres partes. En la primera se analizan las características funcionales y factores ópticos de los vidrios en general. En la segunda se explica qué son los vidrios de baja emisividad, y cómo se obtienen (esto de forma somera), ya que según el proceso de obtención de la capa de baja emisividad queda limitada en mayor o menor grado la trabajabilidad de los vidrios de baja emisividad. Finalmente la tercera parte está dedicada al comportamiento térmico de los acristalamientos en general, y en particular a los huecos acristalados, considerándose el vidrio y la carpintería como una unidad funcional.